Elastic Moduli Data for Polycrystalline Ceramics

About Property Data Summaries.

Database Reference: NIST Structural Ceramics Database, SRD Database Number 30.

Journal Reference:

Elastic Moduli Data for Polycrystalline Ceramics, R. G. Munro, NISTIR 6853, (2002),
National Institute of Standards and Technology,
Gaithersburg, Maryland 20899.
Other Materials: Elastic Moduli Data

Other Materials Properties: Property Data Summaries

ZrO2 · xY2O3(cubic) { zirconium dioxide (cubic), Y-stabilized cubic zirconia, Y-ZrO2(c), ZrO2(cubic,Y) }

Key to the Symbols: T = temperature, d = density, p = volume fraction of porosity, VL = longitudinal sound velocity,
VS = shear sound velocity, E = elastic modulus, G = shear modulus, B = bulk modulus, nu = Poisson's ratio.
Ref.
Nbr.		 Exhibit
Type		 Exhibit
Number		 Value
Type		 Measurement
Method		 Matl.
Nbr.		 T
[°C]		 d
[g/cm3]		 p
[%]		 VL
[km/s]		 VS
[km/s]		 E
[GPa]		 G
[GPa]		 B
[GPa]		 nu Table
Notes
185 Text 904 x ultrasonic resonance 1 23 5.802       222       1
185 Graph 2 x ultrasonic resonance 1 23 5.802       222       1
185 Graph 2 x ultrasonic resonance 1 225         213       1
185 Graph 2 x ultrasonic resonance 1 308         194       1
185 Graph 2 x ultrasonic resonance 1 413         179       1
185 Graph 2 x ultrasonic resonance 1 523         178       1
185 Graph 2 x ultrasonic resonance 1 612         178       1
185 Graph 2 x ultrasonic resonance 1 714         178       1
185 Graph 2 x ultrasonic resonance 1 802         179       1
185 Graph 2 x ultrasonic resonance 1 900         179       1
185 Graph 2 x ultrasonic resonance 1 1014         179       1
185 Graph 2 x ultrasonic resonance 1 1111         178       1
185 Graph 2 x ultrasonic resonance 1 1217         176       1
185 Graph 2 x ultrasonic resonance 1 1297         172       1
185 Graph 2 x ultrasonic resonance 1 1343         170       1
185 Text 904 x ultrasonic resonance 2 23 5.878       223       2
185 Graph 2 x ultrasonic resonance 2 23 5.878       222       2
185 Graph 2 x ultrasonic resonance 2 120         217       2
185 Graph 2 x ultrasonic resonance 2 212         211       2
185 Graph 2 x ultrasonic resonance 2 308         187       2
185 Graph 2 x ultrasonic resonance 2 413         178       2
185 Graph 2 x ultrasonic resonance 2 519         177       2
185 Graph 2 x ultrasonic resonance 2 608         178       2
185 Graph 2 x ultrasonic resonance 2 718         180       2
185 Graph 2 x ultrasonic resonance 2 798         180       2
185 Graph 2 x ultrasonic resonance 2 904         180       2
185 Graph 2 x ultrasonic resonance 2 1014         180       2
185 Graph 2 x ultrasonic resonance 2 1115         179       2
185 Graph 2 x ultrasonic resonance 2 1221         177       2
185 Graph 2 x ultrasonic resonance 2 1301         174       2
185 Graph 2 x ultrasonic resonance 2 1356         171       2

           ===== Table Notes =====

           1: Reported composition (mole fraction): 93.5 % ZrO2 + 6.5 % Y2O3. Relative density was reported as 0.934 .
           2: Reported composition (mole fraction): 93.5 % ZrO2 + 6.5 % Y2O3. Relative density was reported as 0.97 .

Privacy Statement/Security Notice
Disclaimer | FOIA

NIST is an agency of the
U.S. Commerce Department

Date created: 24 October 2002
Last updated: 24 October 2002

Technical inquiries:
Ceramics Division
NIST, 100 Bureau Drive, Stop 8520, Gaithersburg, MD 20899-8520.
Phone (301) 975-6119
Fax (301) 975-5334

Ceramics website comments:
Ceramics Webmaster

General NIST inquiries:
Public Inquiries Unit:
Phone (301) 975-NIST (6478)
TTY (301) 975-8295