Elastic Moduli Data for Polycrystalline Ceramics

About Property Data Summaries.

Database Reference: NIST Structural Ceramics Database, SRD Database Number 30.

Journal Reference:

Elastic Moduli Data for Polycrystalline Ceramics, R. G. Munro, NISTIR 6853, (2002),
National Institute of Standards and Technology,
Gaithersburg, Maryland 20899.
Other Materials: Elastic Moduli Data

Other Materials Properties: Property Data Summaries

ZrO2 · xY2O3 · yFe2O3(c { zirconium dioxide (cubic), Y,Fe-stabilized cubic zirconia, Y,Fe-ZrO2(c), ZrO2(cubic,Y,Fe) }

Key to the Symbols: T = temperature, d = density, p = volume fraction of porosity, VL = longitudinal sound velocity,
VS = shear sound velocity, E = elastic modulus, G = shear modulus, B = bulk modulus, nu = Poisson's ratio.
Ref.
Nbr.		 Exhibit
Type		 Exhibit
Number		 Value
Type		 Measurement
Method		 Matl.
Nbr.		 T
[°C]		 d
[g/cm3]		 p
[%]		 VL
[km/s]		 VS
[km/s]		 E
[GPa]		 G
[GPa]		 B
[GPa]		 nu Table
Notes
186 Table I x ult. pulse echo 1 23 5.2872   3.205 1.62 36.9 13.9 35.8 0.328 1
186 Table I x ult. pulse echo 2 23 5.3057   4.398 2.43 80.1 31.3 60.9 0.28 2
186 Table I x ult. pulse echo 3 23 5.0711   3.345 1.794 42.3 16.3 35 0.298 3
186 Table I x ult. pulse echo 4 23 5.0262   3.38 1.825 43.2 16.7 35.1 0.294 4
186 Table I x ult. pulse echo 5 23 5.011   3.72 1.96 50.5 19.3 43.6 0.308 5
186 Table I x ult. pulse echo 6 23 5.0024   4.418 2.208 65.1 24.4 65.1 0.334 6
186 Table I x ult. pulse echo 7 23 5.02   --- --- --- --- --- --- 7
186 Table I x ult. pulse echo 8 23 5.3303   5.248 2.849 111.8 43.3 89.1 0.291 8
186 Table I x ult. pulse echo 9 23 5.687   3.531 1.852 51.1 19.5 44.9 0.31 9
186 Table I x ult. pulse echo 10 23 5.7175   3.011 1.67 40.6 15.9 30.6 0.278 10
186 Table I x ult. pulse echo 11 23 5.6398   3.475 1.975 55.5 22 38.8 0.261 11
186 Table I x ult. pulse echo 12 23 5.5051   4.926 2.777 107.7 42.5 76.9 0.267 12
186 Table II x ult. pulse echo 1 23 5.6601   --- --- --- --- --- --- 1
186 Table II x ult. pulse echo 2 23 5.6474   4.502 2.481 89.2 34.8 68.1 0.282 2
186 Table II x ult. pulse echo 3 23 5.5385   3.891 2.142 65.2 25.4 49.9 0.283 3
186 Table II x ult. pulse echo 4 23 5.37   3.975 2.175 65.3 25.4 40.9 0.286 4
186 Table II x ult. pulse echo 5 23 5.3109   4.21 2.203 67.6 25.8 59.7 0.311 5
186 Table II x ult. pulse echo 6 23 5.306   --- --- --- --- --- --- 6
186 Table II x ult. pulse echo 7 23 5.147   --- --- --- --- --- --- 7
186 Table II x ult. pulse echo 8 23 5.4875   5.763 3.052 133.4 51.1 114.2 0.305 8
186 Table II x ult. pulse echo 9 23 5.8622   5.267 2.55 102.5 38.1 111.8 0.345 9
186 Table II x ult. pulse echo 10 23 5.787   3.459 1.859 51.9 20 42.5 0.297 10
186 Table II x ult. pulse echo 11 23 ---   --- --- --- --- --- --- 11
186 Table II x ult. pulse echo 12 23 5.5905   5.275 2.961 124.5 49 90.3 0.27 12

           ===== Table Notes =====

           1: Reported composition (mole fraction): 90 % ZrO2 + 10 % Y2O3.
           2: Reported composition (mole fraction): 90 % ZrO2 + 9 % Y2O3 + 1 % Fe2O3.
           3: Reported composition (mole fraction): 90 % ZrO2 + 8 % Y2O3 + 2 % Fe2O3.
           4: Reported composition (mole fraction): 90 % ZrO2 + 7 % Y2O3 + 3 % Fe2O3.
           5: Reported composition (mole fraction): 90 % ZrO2 + 4 % Y2O3 + 6 % Fe2O3.
           6: Reported composition (mole fraction): 90 % ZrO2 + 10 % Fe2O3.
           7: Reported composition (mole fraction): 95 % ZrO2 + 5 % Y2O3.
           8: Reported composition (mole fraction): 95 % ZrO2 + 4 % Y2O3 + 1 % Fe2O3.
           9: Reported composition (mole fraction): 95 % ZrO2 + 3 % Y2O3 + 2 % Fe2O3.
           10: Reported composition (mole fraction): 95 % ZrO2 + 2 % Y2O3 + 3 % Fe2O3.
           11: Reported composition (mole fraction): 95 % ZrO2 + 1 % Y2O3 + 4 % Fe2O3.
           12: Reported composition (mole fraction): 95 % ZrO2 + 5 % Fe2O3.

Privacy Statement/Security Notice
Disclaimer | FOIA

NIST is an agency of the
U.S. Commerce Department

Date created: 24 October 2002
Last updated: 24 October 2002

Technical inquiries:
Ceramics Division
NIST, 100 Bureau Drive, Stop 8520, Gaithersburg, MD 20899-8520.
Phone (301) 975-6119
Fax (301) 975-5334

Ceramics website comments:
Ceramics Webmaster

General NIST inquiries:
Public Inquiries Unit:
Phone (301) 975-NIST (6478)
TTY (301) 975-8295