Elastic Moduli Data for Polycrystalline Ceramics

About Property Data Summaries.

Database Reference: NIST Structural Ceramics Database, SRD Database Number 30.

Journal Reference:

Elastic Moduli Data for Polycrystalline Ceramics, R. G. Munro, NISTIR 6853, (2002),
National Institute of Standards and Technology,
Gaithersburg, Maryland 20899.
Other Materials: Elastic Moduli Data

Other Materials Properties: Property Data Summaries

ZrO2(monoclinic) { zirconium dioxide (monoclinic), zirconia (monoclinic), monoclinic zirconia, ZrO2(m) }

Key to the Symbols: T = temperature, d = density, p = volume fraction of porosity, VL = longitudinal sound velocity,
VS = shear sound velocity, E = elastic modulus, G = shear modulus, B = bulk modulus, nu = Poisson's ratio.
Ref.
Nbr.		 Exhibit
Type		 Exhibit
Number		 Value
Type		 Measurement
Method		 Matl.
Nbr.		 T
[°C]		 d
[g/cm3]		 p
[%]		 VL
[km/s]		 VS
[km/s]		 E
[GPa]		 G
[GPa]		 B
[GPa]		 nu Table
Notes
73 Graph 3 x sonic resonance   24 4.41 0.21     91.6       1
73 Graph 3 x sonic resonance   79         91.5       1
73 Graph 3 x sonic resonance   100         91.5       1
73 Graph 3 x sonic resonance   138         90.9       1
73 Graph 3 x sonic resonance   205         90.2       1
73 Graph 3 x sonic resonance   239         86.3       1
73 Graph 3 x sonic resonance   281         85.1       1
73 Graph 3 x sonic resonance   340         85       1
73 Graph 3 x sonic resonance   386         84.4       1
73 Graph 3 x sonic resonance   415         83.8       1
73 Graph 3 x sonic resonance   458         83.8       1
73 Graph 3 x sonic resonance   483         83.2       1
73 Graph 3 x sonic resonance   496         83.2       1
73 Graph 3 x sonic resonance   512         83.2       1
73 Graph 3 x sonic resonance   533         81.5       1
73 Graph 3 x sonic resonance   554         81.4       1
73 Graph 3 x sonic resonance   575         80.9       1
73 Graph 3 x sonic resonance   592         80.8       1
73 Graph 3 x sonic resonance   706         81.3       1
73 Graph 3 x sonic resonance   287         97.4       2
73 Graph 3 x sonic resonance   160         99.8       2
73 Graph 3 x sonic resonance   29         98.8       2
                               
184 Graph 2 x Flexural res.   25   0.053     197        
184 Graph 2 x Flexural res.   25   0.059     191        
184 Graph 2 x Flexural res.   25   0.061     194        
184 Graph 2 x Flexural res.   25   0.067     184        
184 Graph 2 x Flexural res.   25   0.076     181        
184 Graph 2 x Flexural res.   25   0.1     165        
184 Graph 2 x Flexural res.   25   0.183     108        
184 Graph 2 x Torsional res.   25   0.053       77.9      
184 Graph 2 x Torsional res.   25   0.06       77.9      
184 Graph 2 x Torsional res.   25   0.062       76.5      
184 Graph 2 x Torsional res.   25   0.066       75.2      
184 Graph 2 x Torsional res.   25   0.075       71.7      
184 Graph 2 x Torsional res.   25   0.099       64.5      
184 Graph 2 x Torsional res.   25   0.184       41.9      
184 Graph 2 x 4-pt bending   25   0.055     188        
184 Graph 2 x 4-pt bending   25   0.075     187        
184 Graph 2 x 4-pt bending   25   0.1     155        
184 Graph 2 x 4-pt bending   25   0.183     104        
184 Table III s Flexural res.   50   0.05     199        
184 Table III s Flexural res.   50   0.1     163        
184 Table III s Flexural res.   50   0.15     134        
184 Table III s Flexural res.   50   0.2     110        
184 Table III s Flexural res.   100   0.05     197        
184 Table III s Flexural res.   100   0.1     161        
184 Table III s Flexural res.   100   0.15     132        
184 Table III s Flexural res.   100   0.2     109        
184 Table III s Flexural res.   200   0.05     192        
184 Table III s Flexural res.   200   0.1     158        
184 Table III s Flexural res.   200   0.15     130        
184 Table III s Flexural res.   200   0.2     107        
184 Table III s Flexural res.   400   0.05     181        
184 Table III s Flexural res.   400   0.1     148        
184 Table III s Flexural res.   400   0.15     121        
184 Table III s Flexural res.   400   0.2     99        
184 Table III s Flexural res.   600   0.05     167        
184 Table III s Flexural res.   600   0.1     138        
184 Table III s Flexural res.   600   0.15     114        
184 Table III s Flexural res.   600   0.2     95        
184 Table III s Flexural res.   800   0.05     149        
184 Table III s Flexural res.   800   0.1     128        
184 Table III s Flexural res.   800   0.15     110        
184 Table III s Flexural res.   800   0.2     94        
184 Table III s Flexural res.   1000   0.05     131        
184 Table III s Flexural res.   1000   0.1     113        
184 Table III s Flexural res.   1000   0.15     97        
184 Table III s Flexural res.   1000   0.2     83        
184 Table III s Torsional res.   50   0.05       79      
184 Table III s Torsional res.   50   0.1       65      
184 Table III s Torsional res.   50   0.15       53      
184 Table III s Torsional res.   50   0.2       43      
184 Table III s Torsional res.   100   0.05       78      
184 Table III s Torsional res.   100   0.1       64      
184 Table III s Torsional res.   100   0.15       52      
184 Table III s Torsional res.   100   0.2       42      
184 Table III s Torsional res.   200   0.05       76      
184 Table III s Torsional res.   200   0.1       62      
184 Table III s Torsional res.   200   0.15       50      
184 Table III s Torsional res.   200   0.2       41      
184 Table III s Torsional res.   400   0.05       72      
184 Table III s Torsional res.   400   0.1       58      
184 Table III s Torsional res.   400   0.15       47      
184 Table III s Torsional res.   400   0.2       38      
184 Table III s Torsional res.   600   0.05       66      
184 Table III s Torsional res.   600   0.1       53      
184 Table III s Torsional res.   600   0.15       42      
184 Table III s Torsional res.   600   0.2       34      
184 Table III s Torsional res.   800   0.05       61      
184 Table III s Torsional res.   800   0.1       47      
184 Table III s Torsional res.   800   0.15       37      
184 Table III s Torsional res.   800   0.2       28      
184 Table III s Torsional res.   1000   0.05       53      
184 Table III s Torsional res.   1000   0.1       43      
184 Table III s Torsional res.   1000   0.15       35      
184 Table III s Torsional res.   1000   0.2       28      

           ===== Table Notes =====

           1: On heating.
           2: On cooling.

Privacy Statement/Security Notice
Disclaimer | FOIA

NIST is an agency of the
U.S. Commerce Department

Date created: 24 October 2002
Last updated: 24 October 2002

Technical inquiries:
Ceramics Division
NIST, 100 Bureau Drive, Stop 8520, Gaithersburg, MD 20899-8520.
Phone (301) 975-6119
Fax (301) 975-5334

Ceramics website comments:
Ceramics Webmaster

General NIST inquiries:
Public Inquiries Unit:
Phone (301) 975-NIST (6478)
TTY (301) 975-8295