Elastic Moduli Data for Polycrystalline Ceramics

About Property Data Summaries.

Database Reference: NIST Structural Ceramics Database, SRD Database Number 30.

Journal Reference:

Elastic Moduli Data for Polycrystalline Ceramics, R. G. Munro, NISTIR 6853, (2002),
National Institute of Standards and Technology,
Gaithersburg, Maryland 20899.
Other Materials: Elastic Moduli Data

Other Materials Properties: Property Data Summaries

ZrO2 · xCeO2(tetragonal) { zirconium dioxide (tetragonal), Ce-stabilized tetragonal zirconia polycrystal, Ce-ZrO2(TZP), Ce-TZP, ZrO2(TZP,Ce) }

Key to the Symbols: T = temperature, d = density, p = volume fraction of porosity, VL = longitudinal sound velocity,
VS = shear sound velocity, E = elastic modulus, G = shear modulus, B = bulk modulus, nu = Poisson's ratio.
Ref.
Nbr.		 Exhibit
Type		 Exhibit
Number		 Value
Type		 Measurement
Method		 Matl.
Nbr.		 T
[°C]		 d
[g/cm3]		 p
[%]		 VL
[km/s]		 VS
[km/s]		 E
[GPa]		 G
[GPa]		 B
[GPa]		 nu Table
Notes
189 Table 2 x ult. pulse echo 1 23 6.22   6.71 3.45 195 73.9 180 0.319 1
189 Graph 1 x flexural resonance 1 27 6.22       194       1
189 Graph 1 x flexural resonance 1 78         193       1
189 Graph 1 x flexural resonance 1 97         192       1
189 Graph 1 x flexural resonance 1 148         191       1
189 Graph 1 x flexural resonance 1 198         189       1
189 Graph 1 x flexural resonance 1 223         187       1
189 Graph 1 x flexural resonance 1 299         183       1
189 Graph 1 x flexural resonance 1 401         178       1
189 Graph 1 x flexural resonance 2 37 6.24       194       1
189 Graph 1 x flexural resonance 2 88         193       1
189 Graph 1 x flexural resonance 2 107         192       1
189 Graph 1 x flexural resonance 2 158         191       1
189 Graph 1 x flexural resonance 2 206         188       1
189 Graph 1 x flexural resonance 2 230         188       1
189 Graph 1 x flexural resonance 2 307         183       1
189 Graph 1 x flexural resonance 2 411         179       1
                               
190 Table 2 x ultrasonic velocity   23 5.68       175       2
190 Table 2 x ultrasonic velocity   23 6       179       2
190 Table 2 x ultrasonic velocity   23 6.07       181       2
190 Table 2 x ultrasonic velocity   23 6.01       176       2
190 Table 2 x stress vs. strain   23 5.68       169       2
190 Table 2 x stress vs. strain   23 6       180       2
190 Table 2 x stress vs. strain   23 6.07       175       2
190 Table 2 x stress vs. strain   23 6.01       175       2
                               
191 Table I x flexural resonance 1 27 5.774       122.8       3
191 Table I x flexural resonance 1 -196         142.3       3
191 Table I x flexural resonance 2 27 5.687       107.1       4
191 Table I x flexural resonance 2 -196         130.3       4
191 Table I x flexural resonance 3 27 5.687       115.7       5
191 Table I x flexural resonance 3 -196         132.5       5

           ===== Table Notes =====

           1: Reported composition (mole fraction): 88 % ZrO2 + 12 % CeO2.
           2: Reported composition (mole fraction): 91 % ZrO2 + 9 % CeO2.
           3: Reported composition (mole fraction): 85.5 % ZrO2 + 14.5 % CeO2.
           4: Reported composition (mole fraction): 84.5 % ZrO2 + 15.5 % CeO2.
           5: Reported composition (mole fraction): 83.5 % ZrO2 + 16.5 % CeO2.

Privacy Statement/Security Notice
Disclaimer | FOIA

NIST is an agency of the
U.S. Commerce Department

Date created: 24 October 2002
Last updated: 24 October 2002

Technical inquiries:
Ceramics Division
NIST, 100 Bureau Drive, Stop 8520, Gaithersburg, MD 20899-8520.
Phone (301) 975-6119
Fax (301) 975-5334

Ceramics website comments:
Ceramics Webmaster

General NIST inquiries:
Public Inquiries Unit:
Phone (301) 975-NIST (6478)
TTY (301) 975-8295